>> General Description
Single-component polyurethane waterproof coating is an environmentally friendly reactive polymer waterproof coating, which is uniformly coated on the construction base with tools such as scraper and roller, and can react with moisture and solidified to become a waterproof coating with elastic, strong and durable.
>> Typical Properties
SY-C102P | ||
Type | PU | |
standard | GB/T 19250-2013 | |
Area of construction application | Permanent waterproofing of roof, wall, basement, pool and toilet | |
Apprearance | Black uniform solution | |
Viscosity（23℃） | 6000-8000mPa·S | |
construction time | 60 min | |
Touch free time（23℃） | 5.5-8h | |
Solid content | 90-95％ | |
properties of products | tensile strength | 2.5-3MPa |
elongation at break | 550-1000％ | |
tear strength | 17N/mm² | |
Strength retention rate after acid treatment | >80％ | |
Strength retention rate after alkali treatment | >80％ | |
Strength retention rate after heat treatment | >100％ | |
Elongation after acid treatment | 550% | |
Elongation after alkali treatment | 550% | |
Elongation after heat treatment | 550% | |
Construction condition requirement | 1, avoid construction below 5℃; | |
2, the construction base without clear water; | ||
3. It is necessary to clean the base in advance to remove the floating slurry and dust; | ||
4, the concrete construction is completed for more than 2-3 weeks before the construction of waterproof layer. | ||
>> Storage And Shelf Life
Store in cool and dry warehouse conditions. The storage temperature should be 10℃ -40℃; the storage period is not less than 6 months from the date of production.